Ultramid B3EG6 GIT BK23317
PA6-GF30BASFB3EG6 GIT BK23317 03/2026 PA6-GF30 Guoco Midtown #18-01, 128 Beach Road, Singapore 189773 Ultramid® B3EG6 GIT BK23317 is a glass fiber reinforced and heat stablized PA6 (Black) with enhanced UV resistance.
물성치 데이터
Typical values for uncoloured product at 23°C
| 물성 항목 | 시험 방법 | 단위 | 건조 (Dry) | 조습 (Cond.) |
|---|---|---|---|---|
| properties | ||||
| Polymer abbreviation | - | - | PA6-GF30 | |
| processing | ||||
| Melting temperature, DSC | ISO 11357-1/-3 | °C | 220 | |
| MVR 275 °C/5 kg | ISO 1133 | cm³/10min | 54 | |
| Melt temperature, injection moulding/extrusion | - | °C | 270 - 290 | |
| Mould temperature, injection moulding | - | °C | 80 - 90 | |
| Pre/Post-processing, Pre-drying, Temperature | - | °C | 80 | |
| Pre/Post-processing, Pre-drying, Time | - | h | 2 - 4 | |
| mechanical | ||||
| Tensile modulus | ISO 527-1/-2 | MPa | 9500 | - |
| Stress at break | ISO 527-1/-2 | MPa | 175 | - |
| Strain at break | ISO 527-1/-2 | % | 2.8 | - |
| Flexural modulus | ISO 178 | MPa | 8600 | - |
| Flexural strength | ISO 178 | MPa | 261 | - |
| Charpy unnotched impact strength (23°C) | ISO 179/1eU | kJ/m² | 66 | - |
| Charpy notched impact strength (23°C) | ISO 179/1eA | kJ/m² | 10 | - |
기술 자료
관련 Grade (PA6-GF30)
Glass fibre reinforced and heat aging resistant injection moulding grade, e.g.used for automobile parts with high stiffness requirements under the hood. The products can also be offered as BMBcert™ and/or Ccycled™. Due to the Massbalance approach the product properties do not change.
Deep Gloss D3K R01 BK23361 03/2026 PA Guoco Midtown #18-01, 128 Beach Road, Singapore 189773 Ultramid® Deep Gloss D3K R01 BK23361 is an easy-flowing, UV-stabilized polyamide for injection molding. This grade has excellent surface appearance for high-gloss applications and was designed to offer high level scratch and mar resistance.
D3WG12 Aqua BK00102 03/2026 PA-GF60 BASF Corporation Ultramid® D3WG12 Aqua BK00102 is a 60% glass reinforced, injection molding polyamide offering high strength and stiffness. Due to inherently lower moisture absorption, Ultramid® D3WG12 Aqua BK00102 shows improved retention of
D3EG12 Aqua BK00102 03/2026 PA-GF60 BASF Corporation
B3ZG8 HB BK23309 03/2026 PA6-I GF40 Guoco Midtown #18-01, 128 Beach Road, Singapore 189773 B3ZG8 HB BK23309 is 40% glass fiber reinforced and impact modified PA6 grade for injection molding and high impact applications.
B3ZG7 OSI BK23273 10/2023 PA6-I-GF35 BASF Corporation Ultramid® B3ZG7 OSI BK2373 is a 35% glass reinforced, pigmented black, heat stabilized, impact modified Polyamide 6 injection molding grade. It was developed to meet demanding mechanical and chemical requirements for the automotive oil pan application.